3DPrinting
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: !functionalprint@kbin.social or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
Rules
-
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
-
Be respectful, especially when disagreeing. Everyone should feel welcome here.
-
No porn (NSFW prints are acceptable but must be marked NSFW)
-
No Ads / Spamming / Guerrilla Marketing
-
Do not create links to reddit
-
If you see an issue please flag it
-
No guns
-
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
view the rest of the comments
Not doubting you, but I can't think of a logical reason for why it would be like that. The probe pin shouldn't push down hard enough to be able to deform the PEI
Perhaps as a workaround you could configure the firmware to probe each spot 3 times and average the result, if you don't mind the extra time levelling would take?
I meant the probe is deflected by the texture. Taking multiple sample is what I'm doing, yes. It take at least 5 samples for it to be reasonably smooth, which is why I'm asking other experience.
You mean you think the probe slides off the bumps in the texture? I think the probe should be stiff and light enough to not do that, but perhaps you could've been unlucky if it's a clone not from a well known brand (e.g. Trianglelabs.. even Creality's probe's are supposed to be quite good afaik)
Yes. I'm certain it is a build quality problem. The probe is just plastic and by design hang freely. Even a steel rod with bearing can easily be deflected by a few tens of micron.