3DPrinting
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: !functionalprint@kbin.social or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
Rules
-
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
-
Be respectful, especially when disagreeing. Everyone should feel welcome here.
-
No porn (NSFW prints are acceptable but must be marked NSFW)
-
No Ads / Spamming / Guerrilla Marketing
-
Do not create links to reddit
-
If you see an issue please flag it
-
No guns
-
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
view the rest of the comments
Does the variance return to normal if you switch back to the glass plate? If you probe multiple times on the same spot, do you still get large variance?
Yes to both.
If you press down on the PEI/steel sheet manually, does it look like it's flexing or does it feel stable? When you switched from glass to steel+PEI, did you put an adhesive magnet sheet on the print carriage, or are you using some other method to hold the print surface in place? Just found a post on reddit where someone discovered that their build plate only sticks to the magnetic sheet when they rotate the plate 90 degrees, so perhaps that's worth a try.
Nah it rock solid. The variance come from the texture itself.
Not doubting you, but I can't think of a logical reason for why it would be like that. The probe pin shouldn't push down hard enough to be able to deform the PEI
Perhaps as a workaround you could configure the firmware to probe each spot 3 times and average the result, if you don't mind the extra time levelling would take?
I meant the probe is deflected by the texture. Taking multiple sample is what I'm doing, yes. It take at least 5 samples for it to be reasonably smooth, which is why I'm asking other experience.
You mean you think the probe slides off the bumps in the texture? I think the probe should be stiff and light enough to not do that, but perhaps you could've been unlucky if it's a clone not from a well known brand (e.g. Trianglelabs.. even Creality's probe's are supposed to be quite good afaik)
Yes. I'm certain it is a build quality problem. The probe is just plastic and by design hang freely. Even a steel rod with bearing can easily be deflected by a few tens of micron.